Display事业部以精细图案加工/复制技术和 高分子材料设计/配合技术为基础,开发并提供多种Display用Optical Film。 通过不断研发和Total Solution,满足多变化市场的开发需求。
Optical Film是指在手机、平板、笔记本电脑、车载显示器应用软件中使用的具有各种光学特性的薄膜, 主要以Sheet形态适用于显示器设备。
Application | Model | 亮度 | 厚度 | Remark |
---|---|---|---|---|
|
HLAS-WJ | 100% |
Mobile series : 65㎛, 93㎛ TPC/NB series : 105㎛, 155㎛ Auto series : 155㎛, 218㎛ |
Normal prism |
HLAS-TJ | 105% | |||
HLAS-EJ | 110% | |||
|
XLAS-WJ | 100% |
81 series(MP) : 82㎛ 100 series(MP) : 98 ㎛ 131 series (TPC, NB) : 130㎛ 200 series (TPC, NB) : 180㎛ |
2-in-1 sheet |
XLAS-TJ | 105% | |||
|
YLAS-TJ | 100% |
151 series : 167㎛ 181 series : 195㎛ |
3-in-1 sheet |
YLAS-EJ | 105% |
Application | Model | Haze | 透过率 | 厚度 | Remark |
---|---|---|---|---|---|
|
DLAS-38S1.5 | 95% ± 5% | 60% ± 5% | 53 ㎛ | Non-Bead type |
DLAS-50S1.5 | 95% ± 5% | 60% ± 5% | 64 ㎛ | Non-Bead type |
Application | Model | Haze | 透过率 | 厚度 | Remark |
---|---|---|---|---|---|
|
ALAS-130 | 90% ↑ | 75GU ± 20GU | 129 ㎛ | Non-Bead type |
ALAS-170 | 90% ↑ | 75GU ± 20GU | 169 ㎛ | Non-Bead type |
Application | Model | 厚度 | Haze | 透过率 | Remark |
---|---|---|---|---|---|
|
XLAS-M150L | 159 ㎛ | 99% ±1% | 17% ± 2% | 高辉度 |
XLAS-M180L | 189 ㎛ | ||||
XLAS-M240L | 259 ㎛ | ||||
XLAS-M150H | 159 ㎛ | 99% ±1% | 17% ± 2% | 高屏蔽 | |
XLAS-M180H | 189 ㎛ | ||||
XLAS-M240H | 259 ㎛ |
Application | 亮度 | 均匀度 | 厚度 | 表面硬度 | Color Uniformity (△u'v'_A) |
FOS |
---|---|---|---|---|---|---|
|
达成各型号别成绩书基准 | 80%±5% | 图纸标准 ±0.03 ↓ | 2B ↑ (PC < LGF ≤ PMMA) |
0.015 ↓ | OK |
Application | Model | Type | 透过率 | Haze | Peel stength @glass | Modulus @25℃ | Ink step Coverage |
|
---|---|---|---|---|---|---|---|---|
|
LLAS-N | HD4408 | PSA type | 92% | 0.9% | 1.7 kgf/25㎜ | 0.1 MPa | 30% |
LM1010 | 92% | 0.9% | 1.6 kgf/25㎜ | 0.05 MPa | 35% | |||
HM1008 | 94% | 0.5% | 2 kgf/25㎜ | 0.11 MPa | 30% | |||
|
LLAS-S | SC3106 | UV curable | 92% | 0.5% |
2.2 kgf/25㎜ (*3.4 kgf/25㎜ after post cure) |
0.32 MPa (*after post cure) |
60% |
Application | ITEM | Haze | 透过率 | Pitch | Thickness | Cut-off | Remark |
---|---|---|---|---|---|---|---|
|
PLAS-L1 | 25% | 44% | 45 ㎛ | 210 ㎛ | ≤6% @45˚ | Louver film with Reflective Polarizer |
|
VLAS | 20% | 67% | 39 ㎛ | 300 ㎛ | ≤6% @35˚ | Louver Film for attaching Cover Glass |
|
PLAS-LM40 | 40% | 43% | 39 ㎛ | 415 ㎛ | ≤8% @35˚ | Louver film with Reflective Polarizer |
VLAS-LM40 | 40% | 67% | 39 ㎛ | 305 ㎛ | ≤7% @35˚ | Louver Film | |
VLAS-LV | 22% | 54% | 39 ㎛ | 450 ㎛ | ≤1% @25˚ | Louver Film for CDD (Co Driver Display) |
Application | ITEM | Haze | 可见光偏光 透过率 |
红外线 透射率 |
Thickness | Remark |
---|---|---|---|---|---|---|
|
PLAS-C | 2% | 89% | 73% | 375 ㎛ | HUD用 Cover Lens With Reflective Polarizer |
PLAS-Cv1 | 3% | 81% | 33% | 375 ㎛ | PLAS-C with IR cut-off function |
Application | Peel strength @glass |
Haze | 透过率 | Thickness | Surface Resistivity |
---|---|---|---|---|---|
|
4.0 gf/25㎜ | 0.8% | 92% |
75 ㎛ + 75 ㎛ (PET + PSA) |
Base PET Film Outside : 6x105 Ω PSA : 3x108 Ω |
Application | Peel strength @glass | Haze | 透过率 | Thickness |
---|---|---|---|---|
|
2.2 gf/25㎜ | 0.6% | 91% | 75 ㎛ + 25 ㎛(PET + PSA) |